| 1. Identificação | ||||
| Tipo de Referência | Artigo em Revista Científica (Journal Article) | |||
| Site | mtc-m21d.sid.inpe.br | |||
| Código do Detentor | isadg {BR SPINPE} ibi 8JMKD3MGPCW/3DT298S | |||
| Identificador | 8JMKD3MGP3W34T/44UN7KL | |||
| Repositório | sid.inpe.br/mtc-m21d/2021/06.29.17.54 (acesso restrito) | |||
| Última Atualização | 2021:06.29.17.54.02 (UTC) simone | |||
| Repositório de Metadados | sid.inpe.br/mtc-m21d/2021/06.29.17.54.02 | |||
| Última Atualização dos Metadados | 2022:04.03.23.14.01 (UTC) administrator | |||
| DOI | 10.1016/j.diamond.2021.108507 | |||
| ISSN | 0925-9635 | |||
| Chave de Citação | DalibonMorGuiTraBru:2021:InSuPr | |||
| Título | Influence of the substrate pre-treatment on the mechanical and corrosion response of multilayer DLC coatings  | |||
| Ano | 2021 | |||
| Mês | Oct. | |||
| Data de Acesso | 19 maio 2024 | |||
| Tipo de Trabalho | journal article | |||
| Tipo Secundário | PRE PI | |||
| Número de Arquivos | 1 | |||
| Tamanho | 3150 KiB | |||
| 2. Contextualização | ||||
| Autor | 1 Dalibon, Eugenia L. 2 Moreira, R. D. 3 Guitar, M. A. 4 Trava-Airoldi, Vladimir Jesus 5 Bruhl, S. P. | |||
| Grupo | 1 2 3 4 COPDT-CGIP-INPE-MCTI-GOV-BR | |||
| Afiliação | 1 Universidad Tecnológica Nacional (UTN-FRCU) 2 Universidad Tecnológica Nacional (UTN-FRCU) 3 Saarland University 4 Instituto Nacional de Pesquisas Espaciais (INPE) 5 Universidad Tecnológica Nacional (UTN-FRCU) | |||
| Endereço de e-Mail do Autor | 1 dalibone@frcu.utn.edu.ar 2 3 4 vladimir.airoldi@inpe.br | |||
| Revista | Diamond and Related Materials | |||
| Volume | 118 | |||
| Páginas | e108507 | |||
| Nota Secundária | A1_ENGENHARIAS_IV A1_ENGENHARIAS_II A2_MATERIAIS A2_ENGENHARIAS_III B1_MEDICINA_I B2_QUÍMICA B2_CIÊNCIAS_BIOLÓGICAS_I B2_BIOTECNOLOGIA B2_ASTRONOMIA_/_FÍSICA | |||
| Histórico (UTC) | 2021-06-29 17:54:02 :: simone -> administrator :: 2021-06-29 17:54:03 :: administrator -> simone :: 2021 2021-06-29 17:55:11 :: simone -> administrator :: 2021 2022-04-03 23:14:01 :: administrator -> simone :: 2021 | |||
| 3. Conteúdo e estrutura | ||||
| É a matriz ou uma cópia? | é a matriz | |||
| Estágio do Conteúdo | concluido | |||
| Transferível | 1 | |||
| Tipo do Conteúdo | External Contribution | |||
| Tipo de Versão | publisher | |||
| Palavras-Chave | Corrosion resistance DLC multilayers Martensitic stainless steel Mechanical properties Nitriding as pre-treatment | |||
| Resumo | This work evaluates the mechanical, tribological and corrosion response of single-layer and multilayer DLC films deposited on top of martensitic stainless steel, which was previously plasma nitrided. The efficiency of plasma nitriding as pre-treatment was evaluated using a control group of samples, which was only coated under the same conditions. The pre-treated samples showed a better adhesion of both single and multi-layer DLC films, showing no signs of spallation after applying up to 50 N load during the scratch test. Fretting wear tests (ball on disk) with applied loads 40-70 N were used to evaluate the mechanical response of the different systems. The best response to fretting wear was given by the coatings deposited onto the pre-treated stainless steel substrate, showing a good mechanical stability without cracking up to 70 N load. Additionally, the corrosion resistance evaluated using step-increasing bias potentiostatic tests, turned out to be acceptable when using plasma nitriding as a pre-treatment. On the contrary, the DLC coatings on top of non- pre-treated substrates failed at a potential 400 mV lower than the 1DLC or 5DLC + N samples. Finally, it is seen that combining nitriding with DLC in the form of multilayers constituted the best protective system, since it can delay the formation of pathways between the corrosive solution and the substrate, until 2000 V bias and 3 hours duration of the experiment. | |||
| Área | FISMAT | |||
| Arranjo | urlib.net > BDMCI > Fonds > Produção a partir de 2021 > CGIP > Influence of the... | |||
| Conteúdo da Pasta doc | acessar | |||
| Conteúdo da Pasta source | não têm arquivos | |||
| Conteúdo da Pasta agreement |
| |||
| 4. Condições de acesso e uso | ||||
| Idioma | en | |||
| Arquivo Alvo | dalibon_influence.pdf | |||
| Grupo de Usuários | simone | |||
| Grupo de Leitores | administrator simone | |||
| Visibilidade | shown | |||
| Política de Arquivamento | denypublisher denyfinaldraft24 | |||
| Permissão de Leitura | deny from all and allow from 150.163 | |||
| Permissão de Atualização | não transferida | |||
| 5. Fontes relacionadas | ||||
| Unidades Imediatamente Superiores | 8JMKD3MGPCW/46KUES5 | |||
| Lista de Itens Citando | sid.inpe.br/bibdigital/2022/04.03.23.11 3 | |||
| Divulgação | WEBSCI; PORTALCAPES; COMPENDEX; SCOPUS. | |||
| Acervo Hospedeiro | urlib.net/www/2021/06.04.03.40 | |||
| 6. Notas | ||||
| Campos Vazios | alternatejournal archivist callnumber copyholder copyright creatorhistory descriptionlevel e-mailaddress format isbn label lineage mark mirrorrepository nextedition notes number orcid parameterlist parentrepositories previousedition previouslowerunit progress project resumeid rightsholder schedulinginformation secondarydate secondarykey session shorttitle sponsor subject tertiarymark tertiarytype url | |||
| 7. Controle da descrição | ||||
| e-Mail (login) | simone | |||
| atualizar | ||||